Antibacterial properties of poly (N,N-dimethylaminoethyl methacrylate) obtained at different initiator concentrations in solution polymerization
- Opin vísindi
- →
- IRIS
- →
- IRIS
- →
- Skoða verk
JavaScript is disabled for your browser. Some features of this site may not work without it.
| Titill: | Antibacterial properties of poly (N,N-dimethylaminoethyl methacrylate) obtained at different initiator concentrations in solution polymerization |
| Höfundur: |
|
| Útgáfa: | 2022-01-01 |
| Tungumál: | Enska |
| Umfang: | 654874 |
| Svið: | Engineering and Natural Sciences |
| Deild: | Faculty of Medicine Faculty of Pharmaceutical Sciences |
| Birtist í: | Royal Society Open Science; 9(1) |
| ISSN: | 2054-5703 |
| DOI: | 10.1098/rsos.211367 |
| Efnisorð: | antimicrobial properties; Poly(N,N-dimethylaminoethyl methacrylate); polymerization; Multidisciplinary |
| URI: | https://hdl.handle.net/20.500.11815/3965 |
Tilvitnun:Stawski , D , Rolińska , K , Zielińska , D , Sahariah , P , Hjálmarsdóttir , M A & Másson , M 2022 , ' Antibacterial properties of poly (N,N-dimethylaminoethyl methacrylate) obtained at different initiator concentrations in solution polymerization ' , Royal Society Open Science , vol. 9 , no. 1 , 211367 , pp. 211367 . https://doi.org/10.1098/rsos.211367
|
|
Útdráttur:The samples of poly(N,N-dimethylaminoethyl methacrylate) were synthesized by radical polymerization. The amount of monomer and solvent was constant as opposed to an amount of initiator which was changing. No clear relationship between polymerization conditions and the molecular weight of the polymer was found, probably due to the branched configuration of produced polymer. Bactericidal interactions in all samples against Gram-positive and Gram-negative bacteria have been demonstrated. However, the observed effect has various intensities, depending on the type of bacteria and the type of sample.
|
|